Table of comparisons

Inch (Zoll) / Millimeter

Millimeter / Inch (Zoll)

1/16 in. = 1.59 mm

1/8 in. = 3.17 mm

3/16 in. = 4.76 mm

1/4 in. = 6.35 mm

5/16 in. = 7.94 mm

3/8 in. = 9.52 mm

7/16 in. = 11.11 mm

1/2 in. = 12.70 mm

9/16 in. = 14.29 mm

5/8 in. = 15.87 mm

11/16 in. = 17.46 mm

3/4 in. = 19.05 mm

13/16 in. = 20.64 mm

7/8 in. = 22.22 mm

15/16 in. = 23.81 mm

1 in. = 25.40 mm

1-1/4 in. = 31.75 mm

1-1/2 in. = 38.10 mm

2 in. = 50.80 mm

1 mm = 0.039 in.

2 mm = 0.079 in.

3 mm = 0.118 in.

4 mm = 0.157 in.

5 mm = 0.197 in.

6 mm = 0.236 in.

7 mm = 0.276 in.

8 mm = 0.315 in.

9 mm = 0.354 in.

10 mm = 0.394 in.

11 mm = 0.433 in.

12 mm = 0.472 in.

13 mm = 0.512 in.

14 mm = 0.551 in.

15 mm = 0.590 in.

16 mm = 0.630 in.

17 mm = 0.669 in.

18 mm = 0.709 in.

19 mm = 0.748 in.

20 mm = 0.787 in.

21 mm = 0.827 in.

22 mm = 0.866 in.

23 mm = 0.905 in.

24 mm = 0.944 in.

25 mm = 0.984 in.

25.4 mm = 1 in.

flow-factor 

Wasser: GPM x 3,785 (US) = Liter / Minute
GPM x 4,546 (GB) = Liter / Minute
Luft: SCFM x 28,32 = Liter / Minute

flow-factor 

Cv = 1,17 Kv Kv = 0,86 Cv

torque-factor 

1 Inch Ibs = 0,113 Nm

temperature 

°C

°F

°C

°F

°C

°F

°C

°F

°C

°F

°C

°F

- 200

- 180

- 160

- 140

- 120

- 100

- 95

- 90

- 85

- 80

- 75

- 70

- 65

- 60

- 55

- 50

- 45

- 40

- 35

- 30

- 328

- 292

- 256

- 220

- 184

- 148

- 139

- 130

- 121

- 112

-103

- 94

- 85

- 76

- 67

- 58

- 49

- 40

- 31

- 22

- 25

- 20

- 15

- 10

- 5

+ 0

+ 5

+ 10

+ 15

+ 20

+ 25

+ 30

+ 35

+ 40

+ 45

+ 50

+ 55

+ 60

+ 65

+ 70

- 13

- 4

+ 5

+ 14

+ 23

+ 32

+ 41

+ 50

+ 59

+ 68

+ 77

+ 86

+ 95

+ 104

+ 113

+ 122

+ 131

+ 140

+ 149

+ 158

+ 75

+ 80

+ 85

+ 90

+ 95

+ 100

+ 110

+ 120

+ 130

+ 140

+ 150

+ 160

+ 170

+ 180

+ 190

+ 200

+ 210

+ 212

+ 220

+ 230

+ 167

+ 176

+ 185

+ 194

+ 203

+ 212

+ 230

+ 248

+ 266

+ 284

+ 302

+ 320

+ 338

+ 356

+ 374

+ 392

+ 410

+ 414

+ 428

+ 446

+ 240

+ 250

+ 260

+ 270

+ 280

+ 290

+ 300

+ 310

+ 320

+ 330

+ 340

+ 350

+ 360

+ 370

+ 380

+ 390

+ 400

+ 410

+ 420

+ 430

+ 464

+ 482

+ 500

+ 518

+ 536

+ 554

+ 572

+ 590

+ 608

+ 626

+ 644

+ 662

+ 680

+ 698

+ 716

+ 734

+ 752

+ 770

+ 788

+ 806

+ 440

+ 450

+ 460

+ 470

+ 480

+ 490

+ 500

+ 510

+ 520

+ 530

+ 540

+ 550

+ 560

+ 570

+ 580

+ 590

+ 600

+ 610

+ 620

+ 630

+ 824

+ 842

+ 860

+ 878

+ 896

+ 914

+ 932

+ 950

+ 968

+ 986

+ 1004

+ 1022

+ 1040

+ 1058

+ 1076

+ 1094

+ 1112

+ 1130

+ 1148

+ 1166

+ 640

+ 650

+ 660

+ 670

+ 680

+ 690

+ 700

+ 710

+ 720

+ 730

+ 740

+ 750

+ 760

+ 770

+ 780

+ 790

+ 800

+ 810

+ 820

+ 830

+ 1184

+ 1202

+ 1220

+ 1238

+ 1256

+ 1274

+ 1292

+ 1310

+ 1328

+ 1346

+ 1364

+ 1382

+ 1400

+ 1418

+ 1436

+ 1454

+ 1472

+ 1490

+ 1508

+ 1526

 psi bar psi bar 
 

100 6,89

105 7,23
110 7,58
115 7,92
120 8,27
125 8,61

130 8,96
135 9,30
140 9,65
145 9,99
15010,34

155 10,68
160 11,02
165 11,37
170 11,71
175 12,06

180 12,40
185 12,75
190 13,09
195 13,44
200 13,78

205 14,12
210 14,47
215 14,81
220 15,16
225 15,50

230 15,85
235 16,19
240 16,54
245 16,88
250 17,22

255 17,57
260 17,91
265 18,26
270 18,60
275 18,95

280 19,29
285 19,64
290 19,98
295 20,33
300 20,67

310 21,36
320 22,05
330 22,74
340 23,43
350 24,12

360 24,80
370 25,49
380 26,18
390 26,87
400 27,56

410 28,25
420 28,94
430 29,63
440 30,32
450 31,00

 

460 31,69
470 32,38
480 33,07
490 33,76
500 34,45

510 35,14
520 35,83
530 36,52
540 37,21
550 37,90

560 38,58
570 39,27
580 39,96
590 40,65
600 41,34

610 42,03
620 42,72
630 43,41
640 44,10
650 44,79

660 45,47
670 46,16
680 46,85
690 47,54
700 48,23

710 48,92
720 49,61
730 50,30
740 50,99
750 51,68

760 52,36
770 53,05
780 53,74
790 54,43
800 55,12

810 55,91
820 56,50
830 57,19
840 57,88
850 58,57

860 59,25
870 59,94
880 60,63
890 61,32
900 62,01

910 62,70
920 63,39
930 64,08
940 64,77
950 65,46

960 66,14
970 66,83
980 67,52
990 68,21
1000 68,90

Table of comparisons of the Vickers-Brinell-Rockwell toughness and tensile-strength

Vickershärte

HV 30

Brinellhärte

HB 30

Rockwellhärte2)

HRB    HRC

Zugfestigkeit

oB N/mm2

80

85

90

95

100

105

110

115

120

125

130

135

140

145

150

155

160

165

170

175

180

185

190

195

200

205

210

215

220

225

230

235

240

245

250

255

260

265

270

275

280

285

290

295

300

310

320

330

340

350

360

370

380

390

400

410

420

430

440

450

460

470

480

490

500

510

520

530

540

550

560

570

580

590

600

610

620

630

640

650

660

670

680

690

700

720

740

760

780

800

820

840

860

880

900

920

940

80

85

90

95

100

105

110

115

120

125

130

135

140

145

150

155

160

165

170

175

180

185

190

195

200

205

210

215

220

225

230

235

240

245

250

255

260

265

270

275

280

285

290

295

300

310

320

330

340

350

359

368

376

385

392

400

408

415

423

430

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

36,4      -

42,4      -

47,4      -

52,0      -

56,4      -

60,0      -

63,4      -

66,4      -

69,4      -

72,0      -

74,4      -

76,4      -

78,4      -

80,4      -

82,2      -

83,8      -

85,4      -   

86,8      -

88,2      -

89,6      -

90,8      -

91,8      -

93,0      -

94,0      -

95,0      -

95,8      -

96,6      -

97,6      -

98,2      -

99,0      -

-          19,2

-          20,2

-          21,2

-          22,1

-          23,0

-          23,8

-          24,6

-          25,4

-          26,2

-          26,9

-          27,6

-          28,3

-          29,0

-          29,6

-          30,3

-          31,5

-          32,7

-          33,8

-          34,9

-          36,0

-          37,0

-          38,0

-          38,9

-          39,8

-          40,7

-          41,5

-          42,4

-          43,2

-          44,0

-          44,8

-          45,6

-          46,3

-          47,0

-          47,7

-          48,3

-          49,1

-          49,7

-          50,4

-          51,0

-          51,6

-          52,2

-          52,8

-          53,3

-          53,9

-          54,4

-          55,0

-          55,5

-          56,0

-          56,5

-          57,0

-          57,5

-          58,0

-          58,5

-          59,0

-          59,5

-          60,4

-          61,2

-          62,0

-          62,8

-          63,6

-          64,3

-          65,0

-          65,7

-          66,3

-          66,9

-          67,5

-          68,0

270

290

310

320

340

360

380

390

410

420

440

460

470

490

500

520

540

550

570

590

600

620

640

660

670

680

710

720

730

750

760

780

800

820

830

850

870

880

900

920

940

950

970

990

1010

1040

1080

1110

1140

1170

1200

1230

1260

1290

1320

1350

1380

1410

1430

1460

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

-

1) All toughness values established through various toughness-verification-processes are only approximately comparable.
2) The Rockwell values which appear as decimals only serve the interpolation and should be rounded off at the final result.

Sources: EN ISO 18265